Wear resistance of high Cr white cast irons can be improved by means of heat treatment. The purpose of this work was to study the influence of parameters such as quenching and tempering temperatures and sub zero treatment in the abrasion wear performance of the high Cr white cast iron Nb alloyed. Pin-on-disc abrasion tests were performed and the worn surface was examined by SEM. The main wear mechanisms were identified. This Fe alloy has shown good performance for applications in mining and alcohol-sugar industries.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    The Influence of Heat Treatment on Wear Resistance of High Cr White Cast Iron


    Weitere Titelangaben:

    Sae Technical Papers


    Beteiligte:
    Farah, A. F. (Autor:in) / Canale, L. C. F. (Autor:in) / Crnkovic, O. R. (Autor:in)

    Kongress:

    International Off-Highway & Powerplant Congress ; 2002



    Erscheinungsdatum :

    2002-03-19




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    The influence of heat treatment on wear resistance of high Cr white cast iron

    Canale,L.C. / Farah,A.F. / Crnkovic,O.R. et al. | Kraftfahrwesen | 2002


    Improved Wear Resistance of Austempered Gray Cast Iron Using Shot-Peening Treatment

    Wang, Bingxu / Barber, Gary / Cui, Weiwei et al. | SAE Technical Papers | 2020


    Some experiments on resistance to wear of nitrogenhardened cast iron

    Hurst, J.E. | Engineering Index Backfile | 1933



    Highly wear-resistant cast iron rocker arms - new high-chromium cast iron material

    Kano,M. / Tanimoto,I. / Kawamura,O. et al. | Kraftfahrwesen | 1991