The relationship between hydrogen gas and microporosity in magnesium alloy AZ91 was quantified, refuting the belief that hydrogen levels less than the maximum solid solubility are of no detriment. Sand castings were made from melts containing measured levels of hydrogen gas, and the amount of porosity was determined by density measurements. At concentrations below the maximum solid solubility, it was established that the amount of microporosity is directly proportional to the gas content. This supports the premise that dissolved hydrogen gas provides nucleation sites for microporosity, and that it is useful to remove all gas to achieve porosity-free cast parts.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Interdependence of Hydrogen and Microporosity in Magnesium Alloy AZ91


    Weitere Titelangaben:

    Sae Technical Papers


    Beteiligte:

    Kongress:

    International Congress & Exposition ; 1993



    Erscheinungsdatum :

    01.03.1993




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    Interdependence of hydrogen and microporosity in magnesium alloy AZ91

    Mikucki,B.A. / Shearouse,J.D. / Dow Chemical,US | Kraftfahrwesen | 1993


    The Origin of Microporosity in Magnesium Alloy AZ91

    Mikucki, Barry A. / Shearouse, James D. | SAE Technical Papers | 1994


    The Origin of Microporosity in Magnesium Alloy AZ91

    Shearouse, J. D. / Mikucki, B. A. / Society of Automotive Engineers | British Library Conference Proceedings | 1994


    The origin of microporosity in magnesium alloy AZ91

    Shearouse,J.D. / Mikucki,B.A. / Dow Chemical,US | Kraftfahrwesen | 1994


    Nickel Foam Reinforced AZ91 Magnesium Alloy

    Qiu, K. Q. / Liu, Y. Q. / Suo, Z. Y. et al. | British Library Conference Proceedings | 2007