Thin barium titanate(BT), lead zirconate titanate(PZT), barium strontium titanate(BST) films are being developed for use in microelectronics, electromechanical and optoelectronic applications. Thin BaTiO3, Pb(ZrTi)O3 and (BaSr)TiO3 film capacitor devices were fabricated using RF sputtering techniques. The typical dielectric constant of these film capacitors was in the range of 300 to 1140. These film capacitors had dissipation factors between 0.2% to 0.6 % before annealing and 4-6% after annealing. The film capacitors have breakdown voltages in the range of 1×105 V/cm to 1.2×106 V/cm. The resistivity was in the range of 1010 to 1012 ohm-cm before annealing and 1013 to 1014 ohm-cm after annealing. The capacitance of films produced to-date had little dependence on frequency. Thermal cycling in the temperature range of 50 to 300°C had very limited impact on the capacitance and dissipation factor. Measurements of dielectric and material properties are reported.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Sputtered Barium Titanate, Lead Zirconate Titanate, Barium Strontium Titanate Films for Capacitor Applications


    Weitere Titelangaben:

    Sae Technical Papers


    Beteiligte:

    Kongress:

    Power Systems Conference ; 2000



    Erscheinungsdatum :

    2000-10-31




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    Sputtered Barium Titanate, Lead Zirconate Titanate, Barium Strontium Titanate Films for Capacitor Applications

    Tsao, B.-H. / Carr, S. F. / Heidger, S. et al. | British Library Conference Proceedings | 2000


    Optical-induced absorption tunability of Barium Strontium Titanate film

    Luo, Chunya / Ji, Jie / Yue, Jin et al. | British Library Online Contents | 2016


    Optical-induced absorption tunability of Barium Strontium Titanate film

    Luo, Chunya / Ji, Jie / Yue, Jin et al. | British Library Online Contents | 2016


    Indium Tin Oxide/Barium Strontium Titanate THz Sensor Antenna

    Dittakavi, Sai / Abdel-Motaleb, Ibrahim | IEEE | 2018


    Optical-induced absorption tunability of Barium Strontium Titanate film

    Luo, Chunya / Ji, Jie / Yue, Jin et al. | British Library Online Contents | 2016