By replacing Ni and Mo as alloying elements in sintered steels with Cr and Mn it is possible to achieve high strength at a lower cost for the raw material. Powder compacts containing these elements must however be sintered at high temperatures (around 1250°C) to prevent oxidation. An even carbon content in the sintered parts is reached simply by covering the sintering box with a lid. After single pressing and single sintering at 1250°C for 30 minutes a material containing 1.5% Cr, 0.5% Cu and 0.7% C reaches a tensile strength above 700 N/mm2 and a very small dimensional change (−0.07%) almost independent of the eventual scatter of the carbon content. In order to combine high strength and dimensional precision in the sintered parts the amount and type of alloying additive must be correctly chosen.
High Strength Sintered Steels Containing Chromium and Manganese
Sae Technical Papers
SAE International Congress and Exposition ; 1981
01.02.1981
Aufsatz (Konferenz)
Englisch
High Strength Sintered Steels Containing Chromium and Manganese
Kraftfahrwesen | 1981
|Welding of high chromium steels
SLUB | 1928
|Welding of high chromium steels
TIBKAT | 1928
|Ultrahigh strength and supraductile high-manganese light-weight steels for automotive applications
British Library Conference Proceedings | 2008
|Drilling of Stainless Sintered Steels
SAE Technical Papers | 1998
|