The milling is one of the machining processes with greater employment in the today's industry, because of some aspects such as high rate of material removal and production of workpiece with surface and dimensional accuracy, as well as being a process of high flexibility, being used in the manufacture of flat surfaces, contours, slots and cavities, among others. Among the possible variations of the milling process, one of which has increased employment in the sectors of tooling is currently the top milling. The quality of the machined piece surface depends mainly on the geometry of the tool, of the cutting conditions and of the dynamic behavior of the machine tool. Were conducted tests showing a comparison of the integrity of the machined workpiece surface, with high-speed-steel HSS M2 mills, coated with titanium nitride (TiN), in the machining with minimal quantity of lubricant (MQL). The cut parameter varied was the axial depth of cut (ap), where were used 0.4 and 0.8 mm. The cutting speed was kept constant at 30 m/min. Thus, the objective of this study was to evaluate the surface quality for these cutting conditions.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Analysis of the Surface Integrity in Milling of AISI P20 Steel


    Weitere Titelangaben:

    Sae Technical Papers



    Kongress:

    2008 SAE Brasil Congress and Exhibit ; 2008



    Erscheinungsdatum :

    07.10.2008




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    Analysis of the Surface Integrity in Milling of AISI P20 Steel

    Zeilmann, R.P. / Tome, A. / Antonioli, A. et al. | British Library Conference Proceedings | 2008


    Surface Integrity after Milling Process

    Bordin, Fernando Moreira / Vidor, Matheus / Zeilmann, Rodrigo Panosso et al. | SAE Technical Papers | 2011


    Surface Integrity after Milling Process

    Zeilmann, R.P. / Bordin, F.M. / Vacaro, T. et al. | British Library Conference Proceedings | 2011


    MICROSTRUCTURAL ALTERATION AND MICROHARDNESS AT NEAR-SURFACE OF AISI H13 STEEL BY HARD MILLING

    Zhang, S. / Ding, T.C. / Li, J.F. | British Library Online Contents | 2012


    Predicting Mechanical Properties of Friction Welded AISI 1020/AISI 1018 Steel and AISI 431/AISI 1018 Steel Joints

    Visvalingam, Balasubramanian / Thirumalaikkannan, Dhamothara Kannan / Murugesan, Seeman et al. | SAE Technical Papers | 2023