Development of lightweight alloys suitable for automobile applications has been of great importance to the automotive industry in recent years. The use of 319 type aluminum alloy in the production of gasoline engine blocks is an example of this shift towards light alloys for large automobile components. However, excessive residual stress along the cylinder bores of these engine blocks may cause problems during engine operation. Therefore, in this study, neutron diffraction was used to evaluate residual stresses along the aluminum cylinder bridge and the gray cast iron liners. The strains were measured in the hoop, radial, and axial orientations, while stresses were subsequently calculated using generalized Hooke's law. The results suggest that the residual stress magnitude for the aluminum cylinder bridge was tensile for all three measured components and gradually increased with cylinder depth towards the bottom of the cylinder. The residual stress in the gray cast iron liner was highly compressive with a relatively constant stress magnitude.
Neutron Diffraction Study on Residual Stress in Aluminum Engine Blocks Following Machining and Service Testing
Sae Int. J. Mater. Manf
Sae International Journal of Materials and Manufacturing
SAE 2012 World Congress & Exhibition ; 2012
Sae International Journal of Materials and Manufacturing ; 5 , 1 ; 115-121
2012-04-16
7 pages
Aufsatz (Konferenz)
Englisch
SAE Technical Papers | 2016
|Analysis of Residual Strain Profiles in Distorted Aluminum Engine Blocks by Neutron Diffraction
SAE Technical Papers | 2013
|Internal Residual Stress Measurement of Aluminum Alloy Castings Using Neutron Diffraction
SAE Technical Papers | 2012
|Development of Neutron Residual Stress Measurement of Cast Aluminum Parts
British Library Conference Proceedings | 2008
|