The high temperature strength and deformation behavior of ceramic and two different metal substrates were measured in the 25°-1200°C temperature range in uniaxial and biaxial bending using rectangular bars and circular discs, respectively, prepared from the substrates. The data show that both of the metal substrates exhibit permanent deformation and lose their load carrying capability by an order of magnitude above 800°C. The ceramic substrate, on the other hand, preserves its strength and behaves elastically over the entire temperature range exhibiting neither permanent deformation nor cell distortion. These data suggest that the upper use temperature for metal substrates could be significantly lower than that for ceramic substrates to meet 50-100K vehicle mile durability


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    High Temperature Strength Behavior of Ceramic Versus Metal Substrates


    Weitere Titelangaben:

    Sae Technical Papers


    Beteiligte:

    Kongress:

    International Fuels & Lubricants Meeting & Exposition ; 1990



    Erscheinungsdatum :

    1990-10-01




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    High temperature strength behavior of ceramic versus metal substrates

    Gulati,S.T. / Reddy,K.P. / Thompson,D.F. et al. | Kraftfahrwesen | 1990


    High temperature creep behavior of ceramic and metal substrates

    Gulati,S.T. / Geisinger,K.L. / Reddy,K.P. et al. | Kraftfahrwesen | 1991


    High Temperature Creep Behavior of Ceramic and Metal Substrates

    Thompson, David F. / Reddy, K. Pattabhi / Geisinger, Karen L. et al. | SAE Technical Papers | 1991


    High Temperature Compressive Strength of Extruded Cordierite Ceramic Substrates

    Reddy, K. P. / Gulati, Suresh T. | SAE Technical Papers | 1995


    High temperature compressive strength of extruded cordierite ceramic substrates

    Gulati,S.T. / Reddy,K.P. / Corning Glass,US | Kraftfahrwesen | 1995