An alternative alloy and processing concept has been studied to evaluate the feasibility of producing low-carbon TRIP steels. Conventional hot-rolling, cold-rolling, and batch annealing processes were simulated with three laboratory heats of varying manganese content. The hot-rolled steels were found to be fully hardenable with conventional hot-strip mill processing, and subsequent batch annealing simulations produced significant retained austenite levels. The combination of the prior martensitic microstructure in the as-hot-rolled condition, and subsequent ferrite-martensite-austenite microstructures created by annealing, resulted in remarkable combinations of strength and ductility. Tensile strengths exceeding 1400 MPa were observed in the as-hot-rolled condition, and when annealed at the highest temperatures and longest durations, with total elongations of approximately 10 percent. Ductility increased markedly when samples were annealed at approximately 650°C. While this treatment reduced the tensile strength to 600-1000 MPa, total elongation exceeded 30% in many cases. UTS*TE products greater than 30,000 MPa-% were observed.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Hot- and Cold-Rolled Low-Carbon Manganese TRIP Steels


    Weitere Titelangaben:

    Sae Technical Papers


    Beteiligte:
    Merwin, M. J. (Autor:in)

    Kongress:

    SAE World Congress & Exhibition ; 2007



    Erscheinungsdatum :

    2007-04-16




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    Hot- and cold-rolled low-carbon manganese TRIP steels

    Merwin,M.J. / US Steel Research and Technology Center,US | Kraftfahrwesen | 2007


    Hot- and Cold-Rolled Low-Carbon Manganese TRIP Steels

    Merwin, M. J. / Society of Automotive Engineers | British Library Conference Proceedings | 2007


    Customer oriented development and optimization of cold rolled intercritically annealed multiphase TRIP sheet steels

    Krizan, D. / Traint, S. / Sierlinger, R. et al. | British Library Conference Proceedings | 2008


    High-strength cold-rolled steels

    Parry, B.J. | Tema Archiv | 1984


    Characterization of Cold Rolled TRIP Steels for Structural Crash-Relevant Applications in the Automotive Industry

    Koruk, A. Ihsan / Cretteur, L. / Tosal-Martínez, L. et al. | SAE Technical Papers | 2002