To realize the high performance of the three-way catalyst, this development focused on the heat resistance of the CeO2-ZrO2 solid solution (CZ) that possesses the oxygen storage capacity (OSC). A new concept of the OSC compound with high durability is proposed. We devised a new method of inhibiting the coagulation of the primary CZ particles by placing diffusion barrier layers made of alumina among the primary CZ particles. This material is called “ACZ”.The specific surface area of ACZ was larger than that of the conventional CZ after durability test. The sintering of Pt on the ACZ-added catalyst is inhibited and the crystal size of CZ in the ACZ-added catalyst is smaller than that in the CZ-added catalyst. The OSC and the light off temperature of the ACZ-added catalyst are improved.
Development of Three-way Catalyst Using Composite Alumina-Ceria-Zirconia
Sae Technical Papers
SAE 2003 World Congress & Exhibition ; 2003
03.03.2003
Aufsatz (Konferenz)
Englisch
Development of three-way catalyst using composite alumina-ceria-zirconia
Kraftfahrwesen | 2003
|Development of Three-Way Catalyst Using Composite Alumina-Ceria-Zirconia
British Library Conference Proceedings | 2001
|2003-01-0811 Development of Three-way Catalyst Using Composite Alumina-Ceria-Zirconia
British Library Conference Proceedings | 2003
|Catalytic Soot Oxidation: Effect of Ceria-Zirconia Catalyst Particle Size
SAE Technical Papers | 2016
|Catalytic Soot Oxidation: Effect of Ceria-Zirconia Catalyst Particle Size
British Library Conference Proceedings | 2016
|