Notched bar Izod impact testing of zinc die cast Alloy 3, Alloy 5, ZA-8, and AcuZinc 5 was performed at five temperatures between -40 °C and room temperature in accordance with ASTM E23 for impact testing of metallic materials. A direct comparison between ASTM D256 for impact testing of plastics and ASTM E23 was performed using continuously cast zinc specimens of Alloy 5 and ZA-8 at -40 °C and room temperature. There are differences in sample sizes, impact velocity, and striker geometry between the two tests. Bulk zinc tested according to ASTM E23 resulted in higher impact energies at -40 °C and lower impact energies at room temperature then did the same alloys when tested according to ASTM D256.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Notched Bar Izod Impact Properties of Zinc Die Castings


    Weitere Titelangaben:

    Sae Technical Papers


    Beteiligte:
    Goodwin, F. E. (Autor:in) / Schrems, K. K. (Autor:in) / Doğan, Ö. N. (Autor:in)

    Kongress:

    SAE 2006 World Congress & Exhibition ; 2006



    Erscheinungsdatum :

    03.04.2006




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    Notched bar Izod impact properties of zinc die castings

    Schrems,K.K. / Dogan,O.N. / Goodwin,F.E. et al. | Kraftfahrwesen | 2006


    Izod impact - Does it really mean impact?

    Welgos,R.J. / Caughey,E.C. / Allied Chemical,US | Kraftfahrwesen | 1976


    Izod Impact-Does It Really Mean Impact?

    Caughey, E. C. / Welgos, R. J. | SAE Technical Papers | 1976



    Study of "toss factor" in impact testing of cermets by izod pendulum test

    Probst, H.B. / McHenry, H.T. | Engineering Index Backfile | 1957