In recent years, efforts have “been undertaken to increase the stress load on spring materials and to decrease wire diameter in order to reduce weight. However, progress has “been slow due to the resulting increase in spring sag. This report describes the characteristics of steel wire subjected to a new strain method. After quenching and tempering, while the wire is still warm, strain is imposed on the wire to improve its sag resistance. Results show that sagging in springs made of this wire is approximately one half that of springs made of conventionally quenched and tempered wire of the same strength. Moreover, strain-imposed wire can be quenched and tempered to a lower strength than, yet have the same sag resistance as, extremely high-strength conventional wire. As a result, problems encountered when high strength material is used to improve sag resistance - such as damaged cutting tools and decreased shot peening effect can be avoided. After practical application, the fatigue life of this wire has been confirmed to be sufficient for commercial use.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    High Sag Resistance Spring Wire for Automotive Suspension


    Weitere Titelangaben:

    Sae Technical Papers


    Beteiligte:

    Kongress:

    SAE International Congress and Exposition ; 1985



    Erscheinungsdatum :

    1985-02-01




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    High sag resistance Spring Wire for Automotive suspension

    Murai,T. / Takamuku,S. / Takenoshita,N. et al. | Kraftfahrwesen | 1985


    NEW AUTOMOTIVE-VEHICLE SPRING-SUSPENSION

    Crane, H M | SAE Technical Papers | 1922



    Continous heat treatment of automotive suspension spring steels

    Heitmann, W.E. / Oakwood, T.G. / Krauss, G. | Tema Archiv | 1996


    New system of spring-suspension for automotive vehicles

    Crane, H.M. | Engineering Index Backfile | 1922