The fabrication or repairing of aircraft components made of Hastelloy X to be resolved using an arc welding technique. In this study, Hastelloy X was joint with ERNiCrCoMo-1 filler by pulsed current gas tungsten arc (PCGTA) welding. The high temperature tensile property of the weldment has been evaluated at three different temperatures such as 700 °C, 800 °C and 900 °C. The tensile properties such as yield strength (294, 259 and 205 MPa), ultimate tensile strength (475, 396 and 245 MPa) and percentage of elongation or ductility (17, 14 and 11 %) follows the similar trend with temperature at 700 °C, 800 °C and 900 °C respectively. It revealed the values of all the properties are decreased as the temperature increased. The lowest strength was evaluated for weldment at 900 °C. The high temperature tensile test also revealed that the fracture of weldments for all three conditions is found at the weld centre (WC). Even though, the failure happened at WC, the high temperature tensile strength of the weldments revealed that values are more or less equal to the base metal (Hastelloy X) values at 700 °C, 800 °C and 900 °C. The SEM fractography has been performed to find the tensile failure mode of weldments. The ductile dimples, ductile tear ridges and lesser cleavage-facet are found in the fractured region which derives the ductile failure.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Study on the High Temperature Tensile Properties of Aerospace Grade Hastelloy X Joined by Pulsed Current Arc Welding


    Weitere Titelangaben:

    Sae Technical Papers



    Kongress:

    International Conference on Advances in Design, Materials, Manufacturing and Surface Engineering for Mobility ; 2020



    Erscheinungsdatum :

    2020-09-25




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    Hot Corrosion Demeanour of Key-Hole Plasma Arc Welded Aerospace Grade Hastelloy X in Molten Salts Environment

    Naiju, CD / GokulKumar, Kesavan / Manikandan, Manoharan et al. | SAE Technical Papers | 2020


    A Study of Pulsed Arc Welding Applied to Aerospace Alloys

    R. C. Ashauer / S. Goodman / F. Rienks et al. | NTIS | 1969


    Studies on Metallurgical and Mechanical Properties of Pulsed Current Gas Tungsten Arc Welded Aerospace 80A Grade Alloy

    Natarajan, Arivazhagan / Naiju, CD / Kesavan, Gokul Kumar et al. | SAE Technical Papers | 2021


    High-Frequency, Pulsed-Current GTA Welding

    Roden, William A. | SAE Technical Papers | 1972


    Cryogenic Tensile Properties of Selected Aerospace Materials

    W. Weleff / W. F. Emmons / H. S. McQueen | NTIS | 1964