Friction stability and wear resistance are key factors in brake system design and performance. The paper deals with the experimental investigation of friction characteristics and wear of three commercially available NAO (non-asbestos organic) disc brake friction materials viz. Grade A, Grade B and Grade C for a sport utility vehicle. The composites were evaluated for various friction performance properties such as average coefficient of friction, performance at various speeds (8.34 m/s to 38.89 m/s) and pressures (2 MPa to 12 MPa), fade & recovery behavior. These friction and wear characteristics were determined using four wheeler inertia dynamometer. The physical properties such as density, hardness, heat swell, water swell, adhesive bond strength at room temperature and adhesive bond strength at 400°C were studied according to Indian Standards. In addition SEM-EDX (Scanning electron microscope with energy dispersive X-ray) analysis was carried out for finding ingredients and micro structural characterization of brake friction material. Finally the results are discussed and correlated to the observed friction phenomenon. The coefficient of friction was found to be highest for Grade B and lowest for Grade A and wear of Grade A was lower than that of grades B and C. It was observed that the coefficient of friction increases with increase in speed from 8.34 m/s to 22.23 m/s and then it continuously decreases for speed up to 38.89 m/s. The maximum coefficient of friction was observed at a speed of 22.23 m/s for all the grades viz. A, B and C.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Performance of Non Asbestos Disc Brake Friction Material for Automotive Application - An Experimental Case Study


    Weitere Titelangaben:

    Sae Technical Papers


    Beteiligte:

    Kongress:

    SAE 2010 Annual Brake Colloquium And Engineering Display ; 2010



    Erscheinungsdatum :

    10.10.2010




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    High Performance Asbestos-Free Friction Material for Disc Brake Pads with “The Controlled Grain structure”

    Asano, Hiroshi / Iwata, Kouichi / Kawase, Makoto et al. | SAE Technical Papers | 1989




    A Study of Disc Brake Judder of Non Asbestos Brake Pad

    Abe, K. / Ichikawa, S. / Society of Automotive Engineers of Japan | British Library Conference Proceedings | 1992


    Experimental investigation of disc brake friction

    Ilm,A. / Leung,P.S. / Datta,P.K. et al. | Kraftfahrwesen | 2000