A program for reduced energy consumption in the sintering of iron powder structures has led to development of a copper phosphide alloy additive which enhances diffusion, allowing lower temperature sintering (970°C) while significantly improving strength and ductility. The sinter and strengthening mechanisms, supported by experimental evidence, are explained and compared to conventional iron powder materials.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Strength and Ductility Enhancement of Low Temperature Sintered Iron Powder Structures


    Weitere Titelangaben:

    Sae Technical Papers


    Beteiligte:

    Kongress:

    SAE International Congress and Exposition ; 1982



    Erscheinungsdatum :

    1982-02-01




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    Strength and ductility enhancement of low temperature sintered iron powder structures

    Jandeska,W.F. / General Motors Res.Lab.,US | Kraftfahrwesen | 1982



    High temperature sintered powder metal parts

    Sanderow,H.I. / Management and Engineering Technologies,US | Kraftfahrwesen | 1990


    High Temperature Sintered Powder Metal Parts

    Sanderow, Howard I. | SAE Technical Papers | 1990


    High temperature sintered powder metal parts

    Sanderow, H.I. | Tema Archiv | 1990