The effects of temperature, crack tip opening rate and rubber content on static fracture characteristics of CNBR (Cross-linked acryloNitrile Butadiene Rubber) modified epoxy adhesives were investigated under mode I loading. Loading-unloading tests were statically performed by using DCB (Double Cantilever Beam) specimens.The fracture toughness increased with increasing the rubber content. The fracture toughness of CNBR modified and unmodified epoxy adhesives was much influenced by temperature and crack tip opening rate. The surface topology of fractured surface was changed by temperature and type of adhesive.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Effects of Temperature and Crack Tip Opening Rate on Fracture Behavior of CNBR Modified Epoxy Adhesives Under Mode I Loading


    Weitere Titelangaben:

    Sae Technical Papers


    Beteiligte:
    Kimura, Kazuo (Autor:in) / Naito, Kimiyoshi (Autor:in) / Fujii, Toru (Autor:in)

    Kongress:

    International Congress & Exposition ; 1997



    Erscheinungsdatum :

    1997-02-24




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    Effects of Temperature and Crack Tip Opening Rate on Fracture Behavior of CNBR Modified Epoxy Adhesives Under Mode I Loading

    Kimura, K. / Naito, K. / Fujii, T. et al. | British Library Conference Proceedings | 1997



    Effects of CNBR modification on mode I fracture of epoxy adhesives for automotive applications

    Tsuchida,M. / Naito,K. / Fuji,T. et al. | Kraftfahrwesen | 1995


    Effects of CNBR Modification on Mode I Fracture of Epoxy Adhesives for Automotive Application

    Naito, Kimiyosi / Tsuchida, Masahiro / Fujii, Toru | SAE Technical Papers | 1995