Characterization of aluminum alloy obtained of recycled material is the objective of this study. A aluminum alloy was used to determine the mechanics characteristics and microstructure analyze and their correlation. Specimens were produced to the failure and strength test. Optical and scanning electron microscopy were used the microstructure. In the aluminum alloy was found some porosity that is response for the fragile comportment. The results of the experience were valid when compared with others aluminum alloys in the same fabrication process. In the conclusion of this study perceive that the aluminum alloy have fragile characteristic in function of the heterogeneous composition in associate with the porosity in function of the material that was used to produce the specimen. Perhaps other method of fabrication would can reduce the porosity and increase the mechanics properties de porosities.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Recycled Aluminum: Mechanics and Microestrutural Characterization


    Weitere Titelangaben:

    Sae Technical Papers



    Kongress:

    2008 SAE Brasil Congress and Exhibit ; 2008



    Erscheinungsdatum :

    07.10.2008




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    Recycled Aluminum: Mechanics and Microestructural Characterization

    Fujiyama, R.T. / Darwish, F.A.I. / Society of Automotive Engineers | British Library Conference Proceedings | 2008


    Bending Failure Behavior of Recycled Aluminum Reinforced Composites

    June, B. M. / Pidaparti, R. M. / El-Mounayri, H. | British Library Online Contents | 2001


    Properties of aluminum deposited chemically recycled PET fabrics

    Lee, S. Y. / Hong, T. M. / Jin, D. Y. et al. | British Library Online Contents | 2015



    Performance Characterization of Hot In Recycled Asphalt Mixtures

    Hafeez, I. / Ozer, H. / Al-Qadi, I.L. | British Library Online Contents | 2014