This specification covers an aluminum alloy in the form of sheet 0.010 to 0.249 inch (0.25 to 6.32 mm) inclusive, in nominal thickness, clad on two sides (see 8.4). AMS4256C revises Condition reference specification (3.2), Properties outside specification range (3.3.1.3), Reports (4.4.1) and Identification (5.1.1), and results from a Five-Year Review and update of this specification.
Aluminum Alloy, Clad Two Sides Sheet 0.6Mg - 0.35Si - 0.28Cu (No. 22 Brazing Sheet) As Fabricated
2018-03-23
Aufsatz (Konferenz)
Englisch
Magnesium alloys , Metals , Manganese , Aluminum alloys , Copper , Aluminum , Magnesium , Alloys , Heat treatment , Tensile strength
Aluminum Alloy, Clad Two Sides Sheet 0.6Mg - 0.35Si - 0.28Cu (No. 24 Brazing Sheet) As Fabricated
SAE Technical Papers | 2015
Aluminum Alloy, Clad Two Sides Sheet 0.6Mg - 0.35Si - 0.28Cu (No. 22 Brazing Sheet) As Fabricated
SAE Technical Papers | 2012
Aluminum Alloy, Clad Two Sides Sheet 0.6Mg - 0.35Si - 0.28Cu (No. 22 Brazing Sheet) As Fabricated
SAE Technical Papers | 2023
Aluminum Alloy, Clad Two Sides Sheet 0.6Mg - 0.35Si - 0.28Cu (No. 24 Brazing Sheet) As Fabricated
SAE Technical Papers | 2009
ALUMINUM ALLOY, CLAD TWO SIDES SHEET 0.6Mg - 0.35Si - 0.28Cu (No. 22 Brazing Sheet) As Fabricated
SAE Technical Papers | 1995