Ultrasonic spot welds were made between sheets of 0.8-mm-thick hot-dip-galvanized mild steel and 1.6-mm-thick AZ31B-H24. Lap-shear strengths of 3.0-4.2 kN were achieved with weld times of 0.3-1.2 s. Failure to achieve strong bonding of joints where the Zn coating was removed from the steel surface indicate that Zn is essential to the bonding mechanism. Microstructure characterization and microchemical analysis indicated temperatures at the AZ31-steel interfaces reached at least 344°C in less than 0.3 s. The elevated temperature conditions promoted annealing of the AZ31-H24 metal and chemical reactions between it and the Zn coating.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Ultrasonic Spot Welding of AZ31B to Galvanized Mild Steel


    Weitere Titelangaben:

    Sae Int. J. Mater. Manuf
    Sae International Journal of Materials and Manufacturing


    Beteiligte:
    Brown, Elliot (Autor:in) / Pan, Jwo (Autor:in) / Santella, Michael (Autor:in) / Franklin, Teresa J. (Autor:in) / Pan, Tsung-Yu (Autor:in)

    Kongress:

    SAE 2010 World Congress & Exhibition ; 2010



    Erscheinungsdatum :

    2010-04-12


    Format / Umfang :

    6 pages




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    Ultrasonic Spot Welding of Galvanized Mild Steel to Magnesium AZ31B

    Santella, Michael / Pan, Tsung-Yu | SAE Technical Papers | 2012


    Ultrasonic Spot Welding of Galvanized Mild Steel to Magnesium AZ31B

    Pan, T.-Y. / Santella, M. / Society of Automotive Engineers | British Library Conference Proceedings | 2012


    Expulsion in Resistance Spot Welding of AZ31B Magnesium Alloy

    Zhang, Z. D. / Wang, Y. R. / Li, D. Q. | British Library Conference Proceedings | 2007



    THE SPOT WELDING OF AUTOMOBILE GRADE MILD STEEL

    Wyant, Robert A. / Hess, Wendell F. | SAE Technical Papers | 1940