Samples of commercial powders were sintered at the conventional sintering temperature of 1120°C (2050°F) and also at high temperatures of 1232°C and 1288°C (2250°F and 2350°F) using different time cycles in an industrial walking-beam furnace. Pore morphology is shown in a series of photomicrographs. The spheroidization of pores is rapid at high temperatures and the rate of spheroidization increases with the complexity of powder particles. Pore rounding is also associated with the elimination of prior particle identity as shown in a series of fractographs. High temperature sintered parts, due to improved impact strength and ductility, have potential for expanding the field of powder metallurgy, because parts so processed can be substituted for all but the most demanding forgings and also for nodular iron castings. A nitrogen-base atmosphere of 96:4 N2/H2 composition with a small addition of CO gas performed satisfactorily during high temperature sintering. Dimensional changes were studied and problems connected with dimensional control are discussed.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Changes in Microstructure of Ferrous Powder Metal Compacts During High Temperature Sintering


    Weitere Titelangaben:

    Sae Technical Papers


    Beteiligte:
    Hall, D. W. (Autor:in) / Mocarski, S. (Autor:in)

    Kongress:

    1980 Automotive Engineering Congress and Exposition ; 1980



    Erscheinungsdatum :

    01.02.1980




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    Changes in microstructure of ferrous powder metal compacts during high temperature sintering

    Mocarski,S. / Hall,D.W. / Ford Motor,US | Kraftfahrwesen | 1980


    Isotropic shrinkage of platelet containing glass powder compacts during isothermal sintering

    Boccaccini, A. R. / Conradt, R. | British Library Online Contents | 2001


    The Effects of Hydrogen on Sulfur in Ferrous Compacts

    Sibley, A. Thomas / Marsden, J. G. / Kaiser, John J. | SAE Technical Papers | 1983


    The effects of hydrogen on sulfur in ferrous compacts

    Kaiser,J.J. / Sibley,A.T. / Marsden,J.G. et al. | Kraftfahrwesen | 1983


    SINTERED POWDER METAL PARTS: FERROUS

    SAE Technical Papers | 1973