The effects of working mode, coating weight, thickness of substrate and iron content of coating on the peeling-off resistance of zinc and iron-zinc coatings have been investigated using a draw bead tester, which was designed to evaluate the peeling-off phenomena of coated materials. In the test, specimens are subjected to both bending-unbending deformation and the slide caused by the bead tip. The test was conducted under several working modes; i.e., proportion of the deformation to the slide was changed by altering draw bead conditions.The draw bead results showed that Fe-Zn coating were mainly peeled off by the deformation, while Zn coatings were removed chiefly by the slide. It was also revealed that the amount of peeling-off of the coatings was considerably affected by the working mode.The peeling-off resistance of galvannealed steel sheets was then investigated by the test. The results indicated that the amount of peeling-off was a function of coating weight, thickness of substrate and iron content.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    The Peeling-Off Resistance of Zinc and Iron-Zinc Coated Steel Sheets in Stamping


    Weitere Titelangaben:

    Sae Technical Papers


    Beteiligte:

    Kongress:

    SAE International Congress and Exposition ; 1989



    Erscheinungsdatum :

    01.02.1989




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    The peeling-off resistance of zinc and iron-zinc coated steel sheets in stamping

    Inagaki,J.I. / Nakamura,S. / Yashida,M. et al. | Kraftfahrwesen | 1989




    Frictional and forming behavior of zinc-coated steel sheets

    Siegert,K. / Simon,J. / Institute for Metal Forming Technology,DE | Kraftfahrwesen | 1996


    Frictional and Forming Behavior of Zinc-Coated Steel Sheets

    Simon, Jūrgen / Siegert, Klaus | SAE Technical Papers | 1996