Failure loads of spot welds are investigated under static and impact loading conditions. A test fixture was designed and used to obtain maximum loads of spot welds under a range of combined opening and shear loads with different loading rates. Optical micrographs of the cross sections of spot welds before and after failure were obtained to understand the failure processes under various loading rates and different combinations of loads. The experimental results indicate that under nearly pure opening loads, the failure occurs along the nugget circumferential boundary. Under combined opening and shear loading conditions, the failure starts from the tensile side of the base metal near the nugget in a necking/shear failure mode. The effects of sheet thickness and combined load on the load carrying behavior of spot welds are investigated under static and impact loading conditions based on the experimental results. An engineering failure criterion is proposed to characterize the failure loads of spot welds under combined opening and shear loads for both static and impact loading conditions. The engineering failure criterion is expressed as a function of the nugget size, the sheet thickness, the loading angle for characterization of combined loads, and an empirical coefficient for a given loading rate.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Spot Weld Failure Loads under Combined Mode Loading Conditions


    Weitere Titelangaben:

    Sae Technical Papers


    Beteiligte:
    Pan, J. (Autor:in) / Wung, P. (Autor:in) / Wu, S. (Autor:in) / Lin, S.-H. (Autor:in) / Tyan, T. (Autor:in)

    Kongress:

    SAE 2001 World Congress ; 2001



    Erscheinungsdatum :

    05.03.2001




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    Spot weld failure loads under combined mode loading conditions

    Pan,J. / Wu,S. / Tyan,T. et al. | Kraftfahrwesen | 2001


    Failure Modeling of Spot Welds Under Complex Combined Loading Conditions for Crash Applications

    Pan, J. / Prasad, P. / Lin, S.-H. et al. | SAE Technical Papers | 2002



    The ignored failure mode: spot weld under in-plane rotation ( physical test )

    Wung,P. / Walsh,T. / Ourchan,A. et al. | Kraftfahrwesen | 1999


    The ignored failure mode: spot weld under in-plane rotation (physical test)

    Wung,P. / Walsh,T. / Ourchan,A. et al. | Kraftfahrwesen | 1999