Physical properties of sprayed polyurethane skin for instrument panel were investigated. Optimized sprayed PU(polyurethane) composition for instrument panel was determined by reaction speed measurement, which were polyol of 6000 molecular weight and modified MDI (NCO=25%). For making sprayed PU skin, raw material was sprayed from 15 cm of distance, at 15 g/min of spraying rate, on 70°C of mold, with 75°C of raw material. Sprayed PU skin had lower density than PVC skin when investigating cross sections of skins using scanning electron microscope (SEM). But the reliability test results satisfied all the specification requirements like scratch, chemical resistance, contamination resistance and fogging. Tensile strength, hardness and elongation of sprayed PU skin were slightly changed during heat aging, but the changing rate was much smaller than those of PVC skin.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Physical Properties of Sprayed Polyurethane Skin for Instrument Panel


    Weitere Titelangaben:

    Sae Technical Papers


    Beteiligte:
    Kim, Ok (Autor:in) / Park, Sehong (Autor:in) / Oh, Woojeong (Autor:in) / Chun, Yong (Autor:in)

    Kongress:

    SAE 2005 World Congress & Exhibition ; 2005



    Erscheinungsdatum :

    2005-04-11




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    Physical properties of sprayed polyurethane skin for instrument panel

    Kim,O. / Oh,W. / Chun,Y. et al. | Kraftfahrwesen | 2005


    METHOD FOR MANUFACTURING SKIN MATERIAL FOR INSTRUMENT PANEL AND SKIN MATERIAL FOR INSTRUMENT PANEL

    TAKAI HAJIME / ASAKUMA SHUNTA | Europäisches Patentamt | 2019

    Freier Zugriff

    New Skin for Instrument Panel: SLUSH TPO

    Menard, B. / Valligny, D. | SAE Technical Papers | 1999


    New Skin for Instrument Panel: SLUSH TPO

    Valligny, D. / Menard, B. / Society of Automotive Engineers | British Library Conference Proceedings | 1999


    Chemical recycling of an all-polyurethane instrument panel - industrial realisation

    Kerscher, J. / Schwager, H. / Raßhofer, W. et al. | Tema Archiv | 1996