To aid in better assessing the corrosion performance of AZ91 die cast magnesium, standard salt spray corrosion tests have been made on both randomly selected commercial die castings and on three series of controlled purity test panels. The results reveal that the poor performance often associated with magnesium parts in salt spray are due principally to iron, nickel, and copper contamination levels. When these contaminants were limited, severe pitting corrosion was eliminated and the salt spray performance was good to excellent when compared to 380 aluminum and cold rolled steel.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    The Effects of Heavy Metal Contamination on Magnesium Corrosion Performance


    Weitere Titelangaben:

    Sae Technical Papers


    Beteiligte:

    Kongress:

    SAE International Congress and Exposition ; 1983



    Erscheinungsdatum :

    01.02.1983




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    The effects of heavy metal contamination on magnesium corrosion performance

    Hillis,J.E. / Dow Chemical,Freeport,US | Kraftfahrwesen | 1983


    Effects of heavy metal contamination from anthropogenic sources on Dasarahalli tank, India

    Lokeshwari, H. / Chandrappa, G. T. | British Library Online Contents | 2007


    Spectroscopic Analysis of Heavy Metal Contamination of the Environment

    Miziolek, A. W. / Cespedes, E. R. | British Library Online Contents | 1996


    Corrosion Performance of a Magnesium Tower Brace

    Cahill, James / Redlin, Ken / Lazarz, Kimberly et al. | SAE Technical Papers | 2021


    Corrosion Performance of a Magnesium Tower Brace

    Lazarz, Kimberly / Cahill, James / Ciccone, TJ et al. | British Library Conference Proceedings | 2021