The corrosion resistance of 0 to 15% Ni-Zn electroplated alloy coatings was examined using salt-spray, cyclic corrosion and electrochemical tests. Our findings support those of previous investigations showing that the single phase (gamma) 11 to 15% Ni-Zn coatings provide the best barrier protection for unpainted applications, while the pure Zn coatings provide the highest level of galvanic protection. However, we have found that dual phase (gamma + eta) 9% Ni-Zn coatings appear to provide the best compromise between galvanic and barrier corrosion protection, and a minimum amount of paint delamination. In addition, we found that deformation, similar to body panel stamping, does not have a significant effect on the corrosion resistance of the pure Zn and low Ni-content coatings. However, deformation does produce cracking and a reduction in corrosion resistance for unpainted samples having higher Ni-content coatings.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Corrosion Resistance of 0-15% Ni-Zn Alloy Electroplated Coatings


    Weitere Titelangaben:

    Sae Technical Papers


    Beteiligte:

    Kongress:

    SAE International Congress and Exposition ; 1986



    Erscheinungsdatum :

    01.02.1986




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    ELECTROPLATED COATINGS FOR CONDUCTOR CORROSION RESISTANCE

    SORDELET DANIEL JOSEPH | Europäisches Patentamt | 2025

    Freier Zugriff

    ELECTROPLATED COATINGS FOR CONDUCTOR CORROSION RESISTANCE

    SORDELET DANIEL | Europäisches Patentamt | 2025

    Freier Zugriff

    Corrosion resistance of 0-15% Ni-Zn Alloy electroplated coatings

    Lambert,M.R. / Hart,R.G. / Bethlehem Steel,Homer Research Labs.,US | Kraftfahrwesen | 1986



    Comparative corrosion behavior of electroplated and clad metal coatings

    Baboian,R. / Texas Instruments,Attleboro,US | Kraftfahrwesen | 1980