The work concerns the selection of measurement parameters for selected non-destructive testing methods of Mi helicopter rotor blades after repair. Considered repair cases involve metal cracks in the sandwich skin and repair damage of honeycomb structure (puncture, dent). In the event of a crack, repair is performed by applying a composite-metal repair package. In case of damage of the core, its broken piece is replaced by a new one and then applied the same metal-composite package as in the case of crack repair. The present work focuses on detecting disbond between skin and core below repair patch and cracks under the repair package. Detecting cracks and assessing their length is important because the repair technology provides the repair package without removing of cracked part of skin. Authors have used laser shearography and C-scan methods for MIA and ET. In the methods of eddy currents and mechanical impedance, analysis of the signals collected during the tests was used to determine the optimum parameters. In the laser shearography method, the physical model of the phenomenon occurring during measurement is used to determine the measurement parameters. The research was conducted on equivalent structures. The presented work is part of a program to develop the technology of repairing the rotor blades of the Mi family helicopters.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    The An Approach to Damage Detection in Metal Sandwich Structures with Composite-Metal Patch Bonded Repair


    Weitere Titelangaben:

    Sae Technical Papers


    Beteiligte:

    Kongress:

    AeroTech Congress & Exhibition ; 2017



    Erscheinungsdatum :

    2017-09-19




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    Bonded repair of minimum-gage composite sandwich structures

    Ruddy, J.H. / Vizzini, A.J. | Tema Archiv | 1996


    Approach to Critical Crack Opening Displacement Modeling of Damage in Metal Sheets after Composite Patch Bonded Repair

    Sałacinski Michał / Leski Andrzej / Stefaniuk Michał | DOAJ | 2016

    Freier Zugriff


    Adhesively Bonded Composite Patch Repair of Cracked Aluminium Alloy Structures

    Poole, P. / Young, A. / Ball, A. S. et al. | British Library Conference Proceedings | 1995