The effect of Si-phase on the axial, low-cycle fatigue behavior of Al-Si eutectic alloys was investigated using test specimens prepared from alloys processed either by continuous casting or extrusion. Results indicate that, for continuous casting, all fatigue fractures resulted from shear-type crack initiation and propagation with an attendant shortening of fatigue life. For extruded material, fatigue cracks originated in the Si phase. In both instances, initiation and growth mechanisms were essentially identical to those observed in high-cycle fatigue. Cyclic properties obtained from phenomenological models are presented and discussed.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Low Cycle Fatigue Properties of Al-Si Eutectic Alloys


    Weitere Titelangaben:

    Sae Technical Papers


    Beteiligte:

    Kongress:

    International Congress & Exposition ; 1997



    Erscheinungsdatum :

    1997-02-24




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    Low Cycle Fatigue Properties of Al-Si Eutectic Alloys

    Murakami, Y. / Kobayashi, H. / Ikeda, H. et al. | British Library Conference Proceedings | 1997


    Low cycle fatigue properties of Al-Si eutectic alloys

    Murakami,Y. / Kobayashi,H. / Ikeda,H. et al. | Kraftfahrwesen | 1997


    EUTECTIC WELDING ALLOYS

    MacGillivray, G.A. | SAE Technical Papers | 1943


    Low-cycle fatigue behavior of two magnesium alloys

    Li, Feng / Wang, Yue / Chen, Lijia et al. | Tema Archiv | 2005


    Determining eutectic composition in metal alloys

    Ashbrook, R. L. / Kim, Y. G. | NTRS | 1977