Microstructures and failure mechanisms of spot friction welds (SFW) in aluminum 5754 lap-shear specimens were investigated. In order to study the effect of tool geometry on the joint strength of spot friction welds, a concave tool and a flat tool were used. In order to understand the effect of tool penetration depth on the joint strength, spot friction welds were prepared with two different penetration depths for each tool. The results indicated that the concave tool produced slightly higher joint strength than the flat tool. The joint strength did not change for the two depths for the flat tool whereas the joint strength slightly increases as the penetration depth increases for the concave tool. The experimental results show that the failure mechanism is necking and shearing for the spot friction welds made by both tools. The failure was initiated and fractured through the upper sheet under the shoulder indentation near the crack tip.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Microstructures and Failure Mechanisms of Spot Friction Welds in Lap-Shear Specimens of Aluminum 5754 Sheets


    Weitere Titelangaben:

    Sae Technical Papers


    Beteiligte:
    Pan, J. (Autor:in) / Santella, M. L. (Autor:in) / Lin, P.-C. (Autor:in) / Arul, S. G. (Autor:in) / Pan, T. (Autor:in) / Feng, Z. (Autor:in)

    Kongress:

    SAE 2005 World Congress & Exhibition ; 2005



    Erscheinungsdatum :

    2005-04-11




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch





    Fatigue behaviors of aluminum 5754-O spot friction welds in lap-shear specimens

    Tran,V.X. / Pan,J. / Pan,T.Y. et al. | Kraftfahrwesen | 2008


    Fatigue Behaviors of Aluminum 5754-O Spot Friction Welds in Lap-Shear Specimens

    Pan, Jwo / Pan, Tsung-Yu / Tran, Van-Xuan | SAE Technical Papers | 2008


    Microstructures and Failure Mechanisms of Spot Friction Welds in Lap-Shear Specimens of Aluminum 6111-T4 Sheets

    Pan, J. / Nicholson, J. M. / Garman, M. A. et al. | SAE Technical Papers | 2004


    Microstructures and Failure Mechanisms of Spot Friction Welds in Lap-Shear Specimens of Aluminum 6111-T4 Sheets

    Lin, P-C. / Lin, S-H. / Pan, J. et al. | British Library Conference Proceedings | 2004