In this study, the durability characteristics of three catalyst systems were evaluated. One system was a conventional platinum-rhodium catalyst. The second was a catalyst formulated with palladium and rhodium as the active components. The third system was a catalyst with palladium as the only active metal. These catalysts were evaluated for emissions performance after aging on two durability schedules. The first was a “3-step” aging schedule which is characterized by three distinct temperature steps from 440°C to 775°C. The second schedule involved steady state aging at 440°C. These aging schedules were set up on water-brake engine dynamometers. After low temperature aging, the palladium containing catalysts did not perform as well as the platinum-rhodium catalysts. After 400 hours aging at 440°C, the palladium catalysts had a steady state CO/NOx conversion efficiency of 77% while the platinum rhodium catalyst had a CO/NOx conversion of 95%. It was also observed that this low temperature aging effect was reversible.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Durability Characteristics of Palladium Catalysts


    Weitere Titelangaben:

    Sae Technical Papers


    Beteiligte:

    Kongress:

    International Fuels & Lubricants Meeting & Exposition ; 1991



    Erscheinungsdatum :

    01.10.1991




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    Durability characteristics of palladium catalysts

    Sims,G.S. / General Motors,AV Rochester Div.,US | Kraftfahrwesen | 1991


    Durability of Palladium Only Three-way Automotive Emisson Control Catalysts

    Summers, J. C. / White, J. J. / Williamson, W. B. | SAE Technical Papers | 1989


    Durability of palladium only three-way automotive emission control catalysts

    Summers,J.C. / White,J.J. / Williamson,W.B. et al. | Kraftfahrwesen | 1989


    Durability of extruded electrically heated catalysts

    Weiss,D.S. / Buhrmaster,C.L. / Hampton,L.E. et al. | Kraftfahrwesen | 1995


    Durability of Extruded Electrically Heated Catalysts

    Buhrmaster, Carol L. / Weiss, David S. / Hampton, Leslie E. et al. | SAE Technical Papers | 1995