This paper will illustrate the surface treatment coating that forms a strong metallurgical bond between the titanium alloy matrix regarding the high friction properties and challenging lubricating of titanium alloys. In this research, TC4 has been selected as a base material instead of TiC. Then Ni-composite coating was employed as the surface treatment of TC4 by laser cladding (LC) process. The Ni-based alloy coating material powder is good self-fluxing, has high-temperature resistance, and is analytically pure with 200 mesh. The chemical properties of Ni composite coating include 31.2 % Chromium, 8%Titenium, and 3.6% Carbon. Overall characterization and microstructure analysis of the prepared coating utilizing OM, XRD, SEM, EDS, and EPMA with different laser-specific energies (LSP) performance impact. It is evident that an excellent coating can be employed at the LSP of about 12.5kJ/cm2. The TiC ceramic particle reinforced phase is dispersed into a two-phase solid solution of β-Ti and γ-Ni. The micro-hardness of the employed coating is greater than the base alloy. This research also optimized that laser power is proportional to the coating structure. This research has practical value in the modern aerospace and automobile industry to increase the application of titanium alloy.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Research on Surface Treatment Coating on Titanium Alloy Based on Laser Cladding Technology


    Weitere Titelangaben:

    Sae Int. J. Adv. and Curr. Prac. in Mobility


    Beteiligte:

    Kongress:

    2023 AeroTech ; 2023



    Erscheinungsdatum :

    2023-03-07


    Format / Umfang :

    6 pages




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch





    Laser technologies for coating and cladding

    Pompe,W. / Nowotny,S. / Reitzenstein,W. et al. | Kraftfahrwesen | 1992


    RESEARCH ON WEAR RESISTANCE COATING OF AIRCRAFT TITANIUM ALLOY PARTS BY COLD SPRAYING TECHNOLOGY

    Wenjie Hu / Sergii Markovych / Kun Tan et al. | DOAJ | 2020

    Freier Zugriff

    Melting behavior and tribological properties of titanium-based laser cladding layer WC on the surface of TC4

    ZHANG Tiangang / LI Baoxuan / ZHANG Zhiqiang et al. | DOAJ | 2022

    Freier Zugriff

    Surface performance of TC4 alloy repaired by laser cladding under different scanning speeds

    CUI Jing / WANG Chengxuan / YANG Guangfeng | DOAJ | 2023

    Freier Zugriff