Sulfur oxides endurance and heat resistance of the conventional catalyst were improved from the studies using synthetic model gas and vehicle test. The NOx purification performance was improved for lean NOx catalyst deteriorated due to SOx poising. However, the trapped SOx could be removed with CO in rich gas at 600°C. Moreover, the SOx removal could be promoted with a SOx release material (γ1). On the other hand, heat resistance of the catalyst has been improved by using new mixed metal oxides (C) as a NO2 adsorbent. The improved catalyst which contained γ1 and C showed superior heat resistance at 800°C and SOx durability compared to the conventional lean NOx catalyst in the model gas test. Also, in the vehicle test, the emission values of NOx, HC, and CO were 50% or less than J-ULEV regulation standards. These results show that the improved catalyst has a good purification performance of exhaust gas from a lean burn vehicle.
Improvement of SOx Durability and Heat Resistance for Lean NOx Catalyst
Sae Technical Papers
International Body Engineering Conference & Exhibition and Automotive & Transportation Technology Congress ; 2002
2002-07-09
Aufsatz (Konferenz)
Englisch
Improvement of SOx durability and heat resistance for lean NOx catalyst
Kraftfahrwesen | 2002
|Improvement of Heat Resistance for Lean N0x Catalyst
British Library Conference Proceedings | 2004
|Improvement of Heat Resistance for Lean NOx Catalyst
SAE Technical Papers | 2004
|Improvement of heat resistance for the lean NOx catalyst
Kraftfahrwesen | 2004
|2004-01-1495 Improvement of Heat Resistance for Lean NOx Catalyst
British Library Conference Proceedings | 2004
|