A new high strength aluminium alloy intended for tubes in automotive radiators has been developed. The material is an age hardening alloy containing Mg, Si, Cu, and Mn. Titanium is added for corrosion protection.The post-braze strength of the material is dependent on the cooling rate after brazing. With 1°C/s cooling rate between 400 and 200°C, the Rp0.2 will be about 75 MPa.The corrosion resistance of the material is excellent. It is more noble than standard fin materials and will be protected by sacrificial action. Any attack in the material will be forced into a lamellar mode due to the Ti addition.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    A New High Strength Aluminium Alloy for Controlled Atmosphere Brazing


    Weitere Titelangaben:

    Sae Technical Papers


    Beteiligte:

    Kongress:

    Vehicle Thermal Management Systems Conference & Exposition ; 2001



    Erscheinungsdatum :

    2001-05-14




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    A new high strength aluminium alloy for controlled atmosphere brazing

    Stenqvist,T. / Sapa Heat Transfer,SE | Kraftfahrwesen | 2001


    2001-01-1727 A New High Strength Aluminium Alloy for Controlled Atmosphere Brazing

    Stenqvist, T. / Society of Automotive Engineers | British Library Conference Proceedings | 2001


    A high-strength aluminium alloy fin stock for brazing

    Kawahara,A. / Niikura,A. / Doko,T. et al. | Kraftfahrwesen | 2003


    A high-strength aluminium alloy fin stock for brazing

    Kawahara, A. / Niikura, A. / Doko, T. et al. | British Library Conference Proceedings | 2003


    A high-strength aluminium alloy fin stock for brazing

    Kawahara, A. / Niikura, A. / Doko, T. et al. | Tema Archiv | 2003