This specification, in conjunction with the general requirements for steel heat treatment covered in AMS2759, establishes the requirements for heat treatment of low-alloy steel parts to minimum ultimate tensile strengths of 220 ksi (1517 MPa) and higher. Parts are defined in AMS2759. AMS2759/2E is an update to remove 300M from 3.4.7 and Table 2 Note 2. AMS 2759/2D resulted from a Five Year Review and update to include in Table 2 Note 5 clarification that the snap temper is employed before refrigeration. AMS 2759/2D also included use of marquenching.
Heat Treatment of Low-Alloy Steel Parts Minimum Tensile Strength 220 ksi (1517 MPa) and Higher
2009-07-20
Aufsatz (Konferenz)
Englisch
Heat Treatment of Low-Alloy Steel Parts Minimum Tensile Strength 220 ksi (1517 MPa) and Higher
SAE Technical Papers | 2019
Heat Treatment of Low-Alloy Steel Parts Minimum Tensile Strength 220 ksi (1517 MPa) and Higher
SAE Technical Papers | 2018
HEAT TREATMENT OF LOW-ALLOY STEEL PARTS Minimum Tensile Strength 220 ksi (1517 MPa) and Higher
SAE Technical Papers | 1996
Heat Treatment of Low-Alloy Steel Parts Minimum Tensile Strength 220 ksi (1517 MPa) and Higher
SAE Technical Papers | 2018
Heat Treatment of Low-Alloy Steel Parts Minimum Tensile Strength 220 ksi (1517 MPa) and Higher
SAE Technical Papers | 2021