Simulated turbine blades were subjected to transient and steady-state heating and spanwise loading in a Mach 1 burner rig. Leading-edge cracks were produced which were similar to thermal-fatigue cracks observed during engine service. Crack initiation and propagation data were obtained for a variety of test conditions.The simulated turbine blades consisted of coated and uncoated IN 100 and B 1900 cambered airfoils with grips for application of spanwise load to simulate centrifugal stress. Test variables were blade temperature, spanwise load, and steady-state (hold) time. The Mach 1 gas velocity substantially reduced conventional creep rupture life. This caused a substantial reduction in thermal fatigue life. Coating effectiveness was below that for low velocity tests.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Thermal Fatigue Testing of Simulated Turbine Blades


    Weitere Titelangaben:

    Sae Technical Papers


    Beteiligte:
    Spera, D. A. (Autor:in) / Calfo, F. D. (Autor:in) / Bizon, P. T. (Autor:in)

    Kongress:

    National Air Transportation Meeting ; 1971



    Erscheinungsdatum :

    01.02.1971




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    High-Temperature Fatigue Testing of Turbine Blades

    Kopec Mateusz / Kukla Dominik / Wyszkowski Mirosław et al. | DOAJ | 2024

    Freier Zugriff

    Thermal-Transient Testing Of Turbine Blades

    Wagner, William R. / Pidcoke, Louis H. | NTRS | 1990



    Fatigue Testing of 9 m Carbon Fiber Wind Turbine Research Blades

    Paquette, Joshua / van Dam, Jeroen / Hughes, Scott et al. | AIAA | 2008


    Fatigue Testing of 9 m Carbon Fiber Wind Turbine Research Blades

    Paquette, J. / van Dam, J. / Hughes, S. et al. | British Library Conference Proceedings | 2008