The relative machinability of four low carbon, resulfurized, rephosphorized free cutting steels (1215, 12L14, 1214+0.1wt%Bi & 1214+0.2wt%Bi) were evaluated using a modified ASTM E618 machine form tool wear test.The chemical, mechanical and micro-structural characteristics of these four steels are compared and correlated to the machining performance.The 1215 consistently survived 8 hours machining at 77.4m/min (meters/minute)[(254sfpm (surface feet per minute)] and 4 of 6 tests passed 8 hours at 85.3m/min (280sfpm). The 12L14 survived 8 hours at 85.3m/min (280sfpm), but consistently failed the test at 95.1m/min (312sfpm). The 1214+0.1wt%Bi consistently survived 8 hours at 95.1m/min (312sfpm), but failed at 111m/min (364sfpm). The 1214+0.2wt%Bi also survived 8 hours at 95.1m/min (312sfpm) and one of six tests passed 8 hours at 111m/min (364sfpm).At each test speed the rough form tool and finish form tool generated surface roughness (Ra) was monitored. The Ra of the rough form tool generated surface was highest for 1215 and smoothest for 1214+0.2wt%Bi. The Ra of the finish form tool generated surface was found to be the smoothest for the 1215.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Comparative Machinability of Bloom Cast Free Cutting Steels


    Weitere Titelangaben:

    Sae Technical Papers


    Beteiligte:
    Vea, Lynn (Autor:in)

    Kongress:

    International Congress & Exposition ; 1997



    Erscheinungsdatum :

    1997-02-24




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch


    Schlagwörter :


    Comparative machinability of bloom cast free cutting steels

    Vea,L. / Inland Steel Bar,US | Kraftfahrwesen | 1997


    Comparative Machinability of Bloom Cast Free Cutting Steels

    Vea, L. / SAE | British Library Conference Proceedings | 1997


    Comparative machinability of brasses, steels and aluminium alloys:CDAs universal machinability index

    Thiele,E.W. / Kundig,K.J. / Murphy,D.W. et al. | Kraftfahrwesen | 1990


    Comparative Machinability of Brasses, Steels and Aluminum Alloys: CDA's Universal Machinability Index

    Duffin, Brian / Murphy, Donald W. / Thiele, Eugene W. et al. | SAE Technical Papers | 1990


    New multiphase steels with excellent machinability

    Roelofs, H. / Urlau, U. / Lembke, M. et al. | British Library Conference Proceedings | 2008