Failure surfaces of glass fiber-reinforced sheet molding compounds (SMC) adhesively bonded to metal brackets were examined by scanning electron microscopy. The adhesive was shown to fail by mixed modes of tear and brittle fracture, probably due to an unusual microstructural morphology which also contributed to a decrease in its fracture toughness at elevated temperatures. The SMC failure mode of the substrate was shown to be delamination by tear. For the debonded joints, a range of failure modes were observed, from simple adhesive failure to substrate delamination beneath the bondline. Wetting of the SMC substrate was found to be inadequate, probably due to the high viscosity of the adhesive, leading to inadequate interdiffusion between the adhesive and the adherend. In some samples, the SMC substrate was found to have delaminated directly beneath the bondline, to a depth of one to two times the diameter of the glass fiber. The results demonstrated that an interdisciplinary program to study the chemical, interfacial and mechanical properties of the various components in adhesive joints is needed.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Fractography of Adhesively Bonded SMC-Metal Joints


    Weitere Titelangaben:

    Sae Technical Papers


    Beteiligte:

    Kongress:

    1988 Conference and Exposition on Future Transportation Technology ; 1988



    Erscheinungsdatum :

    1988-08-01




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    Fractography of adhesively bonded SMC-metal joints

    Leung,C.L. / Rockwell International,US | Kraftfahrwesen | 1988



    Failure Analysis of Adhesively Bonded Joints

    Sheppard, A. / Kelly, D. / Rose, F. et al. | British Library Conference Proceedings | 1995


    Preliminary Design Of Adhesively Bonded Composite Joints

    Chamis, C. C. / Murthy, P. L. N. | NTRS | 1992


    Health monitoring approach for adhesively bonded joints

    Salamone, Salvatore / Fasel, Tim / Bartoli, Ivan et al. | Tema Archiv | 2009