The purpose of this recommended practice is to provide the aerospace industry with recommendations concerning minimizing stress-corrosion cracking (SCC) in wrought high-strength aluminum alloy products.
Minimizing Stress-Corrosion Cracking in Wrought Heat-Treatable Aluminum Alloy Products