The increasing durability requirements for aluminum heat exchangers involve the use of higher levels of magnesium in the core material in order to increase the strength of its components. The challenge is to braze these aluminum alloys by the preferred CAB process.During the CAB process magnesium diffuses out, forming a Magnesium Oxide and Magnesium Fluorides and the use of conventional flux becomes ineffective for disrupting it. When wetting occurs, the brazed joint is discontinuous and the presence of leaks becomes more probable.It was found that using a modified aluminum flux that includes some cesium in its composition for aluminum controlled atmosphere-brazing process, it is possible to obtain strong brazed joints on the heat exchangers. Additionally, the inclusion of cesium in the flux makes possible to braze aluminum alloys with higher levels of magnesium providing stronger and more durable heat exchangers assemblies.In this work, it was tested the cesium flux on plate to plate specimens, on mock-ups in our CAB laboratory furnace, and in complete heat exchangers in the standard production line. The results and future work with cesium flux are presented.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Brazeability of Aluminum Alloys Containing Magnesium by CAB Process Using Cesium Flux


    Weitere Titelangaben:

    Sae Technical Papers


    Beteiligte:
    Massoulier, C. (Autor:in) / Garcia, J. (Autor:in) / Faille, Ph. (Autor:in)

    Kongress:

    Vehicle Thermal Management Systems Conference & Exposition ; 2001



    Erscheinungsdatum :

    14.05.2001




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    Brazeability of aluminium alloys containing magnesium by CAB process using cesium flux

    Garcia,J. / Massoulier,C. / Faille,P. et al. | Kraftfahrwesen | 2001


    2001-01-1763 Brazeability of Aluminum Alloys Containing Magnesium by CAB Process Using Cesium Flux

    Garcia, J. / Massoulier, C. / Faille, P. et al. | British Library Conference Proceedings | 2001


    Improvement in the Brazeability of Aluminum Clad Thinner Fin for Automotive Heat Exchanger

    Toyama, Taketoshi / Shoji, Yoshifusa / Hasegawa, Yoshiharu et al. | SAE Technical Papers | 2005


    Vacuum Brazing: Effect of Oxide Conditions on Brazeability

    Wittebrood, A. / Van der Veldt, T. / Vieregge, K. et al. | British Library Conference Proceedings | 1997


    Improvement in the brazeability of aluminum clad thinner fin for automotive heat exchanger

    Hisatomi,Y. / Shoji,Y. / Toyama,T. et al. | Kraftfahrwesen | 2005