Durability performance characteristics of copper-containing base metal catalysts and base metal/low noble metal catalysts have been determined in laboratory and engine aging conditions under well controlled stoichiometric closed-loop A/F operation.Cu-Cr base metal formulations yield significant HC and CO conversions under stoichiometric operation after aging at 620°C, but deteriorate rapidly at high-temperature (750°C inlet) stoichiometric operation. Incorporation of Rh into the base metal formulation substantially improved NOx performance, a major weakness of base metal catalysts. The addition of Cu-Cr base metals substantially improves CO oxidation over Pt, Pd, and Rh catalysts but was accompanied by some loss of HC conversion over Pt and Rh. A Cu-Cr/Pd catalyst, however, also had better HC conversions as well as significantly improved light-off performance when compared to a Pd-only catalyst.The stoichiometric operating strategy and performance envelope for base metal catalysts were probed in engine dynamometer and vehicle studies. The aged performance of the Cu containing catalysts is significantly lowered by lean A/F preconditioning due probably to sulfur poisoning of Cu at low-temperature lean operating conditions.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Performance of Copper Base Metal Catalysts in Stoichiometric Automotive Exhausts


    Weitere Titelangaben:

    Sae Technical Papers


    Beteiligte:
    Summers, J. C. (Autor:in) / White, J. J. (Autor:in) / Marinangeli, R. E. (Autor:in) / Williamson, W. B. (Autor:in)

    Kongress:

    1987 SAE International Fall Fuels and Lubricants Meeting and Exhibition ; 1987



    Erscheinungsdatum :

    1987-11-01




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    Performance of copper base metal catalyst in stoichiometric automotive exhausts

    Williamson,W.B. / Summers,J.C. / White,J.J. et al. | Kraftfahrwesen | 1987


    Plasma-Enhanced Catalysis for Automotive Exhausts

    Rich, J. William / Wodzisz, Ken / Abrams, Lisa M. et al. | SAE Technical Papers | 1997


    PM stainless steels uses in automotive exhausts

    Causton, R.J. / Mumau, C. / Cimino, T.M. | Tema Archiv | 1998


    UV-based pollutant quantification in automotive exhausts [6198-06]

    Hawe, E. / Dooly, G. / Fitzpatrick, C. et al. | British Library Conference Proceedings | 2006


    Particle Number Reduction in Automotive Exhausts Using Acoustic Metamaterials

    Katoshevski, David / Boden, Hans / Abom, Mats et al. | SAE Technical Papers | 2017