The ambient temperature aging behavior of hot dip coated cold-rolled bake hardenable steel sheets manufactured by an in-line continuous annealing technique has been investigated. These materials exhibit good and uniform mechanical and bake hardening properties as-produced and after aging. For the same chemistry, carbon and nitrogen solute levels can be higher in galvanized (GI) products than in galvannealed (GA) products, with the result, of course, of higher bake hardening and aging indexes. Based on the classical static strain aging theory, the interactions between interstitial solutes and dislocations during the ambient aging of these steel sheets can be classified into four stages. Optimal press forming or stamping operations are best performed in the first or second stages of aging but no significant forming difficulties should be expected even if these operations are conducted during the later aging stages.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Ambient Aging Behavior of Hot Dip Coated Bake Hardenable Steel Sheets Relevant to Automotive Industry


    Weitere Titelangaben:

    Sae Technical Papers


    Beteiligte:
    Smith, G.M. (Autor:in) / Denner, S.G. (Autor:in) / Sun, W.P. (Autor:in)

    Kongress:

    International Congress & Exposition ; 1999



    Erscheinungsdatum :

    01.03.1999




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    Ambient Aging Behavior of Hot Dip Coated Bake Hardenable Steel Sheets Relevant to Automotive Industry

    Sun, W. P. / Smith, G. M. / Denner, S. G. et al. | British Library Conference Proceedings | 1999



    Development of Cu-bearing bake-hardenable steel sheets for automotive exposed panels

    Hong, Moon-Hi / Cho, Noi-Ha / Kim, Sung-Il et al. | Tema Archiv | 2010


    Bake Hardenable Continuous Annealed Drawing Steel Grades

    Prum,N. / Meers,U. / Verhoeven,G. et al. | Kraftfahrwesen | 1986


    Recent development in bake-hardenable sheet steel for automotive body panels

    Mizui,N. / Okamoto,A. / Tanioko,T. et al. | Kraftfahrwesen | 1990