The effect of temperature and preload on the bolt load retention (BLR) behavior of AZ91D and AE42 magnesium die castings was investigated. The results were compared to those of 380 aluminum die castings. Test temperatures from 125 to 175°C and preloads from 7 to 28 kN were investigated. The loss of preload for AZ91D was more sensitive to temperature than that observed for AE42, especially at low preloads. In general, retained bolt-load was lowest in AZ91D. All test assemblies were preloaded at room temperature and load levels increased when the assemblies reached test temperature. The load-increase was dependent on the preload level, test temperature, alloy, and results from thermal expansion mismatch between the steel bolt and the magnesium alloy components, mitigated by the onset of primary creep. Thermal exposure (aging) of AZ91D at 150°C improved BLR behavior.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Bolt-Load Retention Behavior of Die-Cast AZ91D and AE42 Magnesium


    Weitere Titelangaben:

    Sae Technical Papers


    Beteiligte:
    Yurko, J.A. (Autor:in) / Allison, J.E. (Autor:in) / Kearns, J.E. (Autor:in) / Jones, J.W. (Autor:in) / Sohn, K.Y. (Autor:in)

    Kongress:

    International Congress & Exposition ; 1998



    Erscheinungsdatum :

    1998-02-23




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    Bolt-load retention behavior of die-cast AZ91D and AE42 magnesium

    Sohn,K.Y. / Yurko,J.A. / Jones,J.W. et al. | Kraftfahrwesen | 1998


    Cast Magnesium Subframe Development - Bolt Load Retention

    Wagner, David / Heath, Gerald / Uicker, John et al. | SAE Technical Papers | 2021


    Creep and Bolt-Load Retention Behavior of Die-Cast Magnesium Alloys

    Sohn, K. Y. / Yurko, J. A. / Chen, D. C. et al. | British Library Conference Proceedings | 1998



    Bolt-load retention behavior of a die cast magnesium-rare earth alloy

    Moreno,I.P. / Sohn,K.Y. / Jones,J.W. et al. | Kraftfahrwesen | 2001