Coating mass losses occurring on two galvannealed sheet steel samples, one with and one without significant amounts of zeta in the coating, were measured in draw bead simulator tests at different bead penetrations, sliding speeds and with different amounts of oil on the surface. Coating mass losses were small relative to the coating weight. The galvanneal coating without zeta exhibited a greater mass loss than the coating with zeta. Bead penetration was an important variable affecting coating mass loss in both coils, and through an interaction with sliding speed in one coil. Compressive strains due to bending and unbending are the primary cause for coating mass loss; sliding friction did not enhance coating mass loss. The quantitative results are compared with coating mass losses that occur in other formability tests.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Galvanneal Powdering in Drawbeads


    Weitere Titelangaben:

    Sae Technical Papers


    Beteiligte:
    Rangarajan, V. (Autor:in)

    Kongress:

    International Congress & Exposition ; 1997



    Erscheinungsdatum :

    24.02.1997




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    Galvanneal powdering in drawbeads

    Rangarajan,V. / Bethlehem Steel,US | Kraftfahrwesen | 1997


    Galvanneal Powdering in Drawbeads

    Rangarajan, V. / SAE | British Library Conference Proceedings | 1997


    Corrosion and Powdering Resistance of Galvanneal

    Chou, K. / Jagannathan, V. / NACE; Task Group T-14A on Automotive Corrosion | British Library Conference Proceedings | 1992


    Correlation of Prephosphate Treatment, Surface Friction and Powdering of Galvanneal During Forming

    Michal, G. M. / Saran, M. J. / Kunde, N. D. | SAE Technical Papers | 1998


    Correlation of prephosphate treatment, surface friction and powdering of galvanneal during forming

    Kunde,N.D. / Saran,M.J. / Michal,G.M. et al. | Kraftfahrwesen | 1998