Hypervelocity impact damage on pressurized aluminum alloy tanks, due to orbital debris, was studied. The induced damaged area, as the results of the fragmented particles, was measured. The calculated damaged size was incorporated in the FMDM (fracture mechanics of ductile metals) model to predict catastrophic failure. The variation of the failure stress as a function of critical damaged size was plotted and was called damaged or failure curve. The failure predicted by the model collaborated with the experimental test results performed on several plates. These plates were subjected to biaxial loading simulated state of stress induced in the cylindrical pressurized tank.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Damage Propagation in Ductile Metals Subjected To Hypervelocity Impacts


    Weitere Titelangaben:

    Sae Technical Papers


    Beteiligte:

    Kongress:

    Aerospace Technology Conference and Exposition ; 1990



    Erscheinungsdatum :

    01.09.1990




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    Hypervelocity Impacts and Damage Laws

    Lambert, M. / COSPAR; Scientific Commission B | British Library Conference Proceedings | 1997


    Hypervelocity Impacts and Damage Laws

    Lambert, M. | Online Contents | 1997


    Response of ETFE Sheets Subjected to Hypervelocity Impacts

    Nitta, K. / Higashide, M. / Takeba, A. et al. | British Library Conference Proceedings | 2013


    Hypervelocity impacts

    Online Contents | 1997


    Response of a Aluminum Honeycomb Subjected to Hypervelocity Impacts

    Nitta, Kumi / Higashide, Masumi / Kitazawa, Yukito et al. | Tema Archiv | 2013