The fatigue strength and failure behavior of A5754-O adhesively bonded single lap joints by a hot-curing epoxy adhesive were investigated in this paper. The single lap joints tested include balanced substrate joints (meaning same thickness) and unbalanced substrate joints, involving combinations of different substrate thicknesses. Cyclic fatigue test results show that the fatigue strength of bonded joints increase with the increasing substrate thickness. SEM and Energy Dispersive X-ray (EDX) were employed to investigate the failure mode of the joints. Two fatigue failure modes, substrate failure and failure within the adhesive were found in the testing. The failure mode of the joint changes from cohesive failure to substrate failure as the axial load is decreased, which reveals a fatigue resistance competition between the adhesive layer and the aluminum substrate.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    An Investigation on the Fatigue Behavior of Balanced and Unbalanced Epoxy-Aluminum Single Lap Joints


    Weitere Titelangaben:

    Sae Technical Papers


    Beteiligte:
    Guo, Haiding (Autor:in) / Hill, John (Autor:in) / Bonnen, John J. (Autor:in) / Lasecki, John V. (Autor:in) / Chen, Qiuren (Autor:in) / Su, Xuming (Autor:in)

    Kongress:

    SAE 2015 World Congress & Exhibition ; 2015



    Erscheinungsdatum :

    2015-04-14




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch





    Unbalanced-to-Balanced Video Interface

    Richardson, J. E. | NTRS | 1986


    Fatigue behavior of weldbonded joints

    SCARICH, G. V. / CHANANI, G. R. | AIAA | 1982


    Effects of Compression-Compression Fatigue Balanced Graphite/Epoxy Laminates with Holes

    James W. Mar / Michael J. Graves / David P. Maass | AIAA | 1981


    Fatigue Performance of Aluminum Joints for Automotive Applications

    Nordmark, G. E. | SAE Technical Papers | 1978