The interference-fit processing and split-sleeve cold expansion processing were employed on the 7050-T7451 aluminum alloy joints and fatigue test of joints were carried out. The effects of the processing on fatigue life were compared and characteristics of fatigue fracture appearance were studied by scanning electron microscope.The results show that the interference-fit bolted joints obtain longer fatigue life with interference of 0.08∼0.14mm, the longest with 0.11mm, and the fatigue life of split-sleeve cold expanded bolted joints increase with hole cold expansion of 3-5%'s growth. The maximum fatigue life is increased to 3 times that of the non- cold worked joints.The fatigue crack fractography present the characteristics of mixed transgranular fracture and material of 7050-T7451 has toughness. Interference-fit and split-sleeve cold expansion processing can also strengthen the wall of hole and make fatigue crack source from the surface of structure, not the wall of the hole.Split-sleeve cold expansion processing can be beneficial for increasing the fatigue life better.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Effect of Strengthened Hole on the Fatigue Life of 7050-T7451 Double-Shear Joints


    Weitere Titelangaben:

    Sae Technical Papers


    Beteiligte:
    Huang, Hong (Autor:in) / Xiao, Qingdong (Autor:in) / Zhao, Qingyun (Autor:in)

    Kongress:

    SAE 2013 AeroTech Congress & Exhibition ; 2013



    Erscheinungsdatum :

    17.09.2013




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    Effect of Strengthened Hole on the Fatigue Life of 7050-T7451 Double-Shear Joints

    Zhao, Q. / Huang, H. / Xiao, Q. et al. | British Library Conference Proceedings | 2013


    Fatigue life prediction for 7050-T7451 aluminum alloy plate with scratch defect

    Zhan, Zhixin / Hu, Weiping / Zhang, Miao et al. | British Library Online Contents | 2015


    Research on 7050-T7451 Shear Angle Correction Model Based on Anisotropic Features

    Li, Duoduo / Pan, Yongzhi / Li, Hongxia et al. | IEEE | 2020



    Issues on the mean stress effect in fretting fatigue of a 7050-T7451 Al alloy posed by new experimental data

    Rossino, L.S. / Castro, F.C. / Bose Filho, W.W. et al. | Tema Archiv | 2009