In the present experimental investigation magnesium based alloy was prepared by mixing magnesium powder and aluminium powder in the ratio 65:35. The prepared magnesium alloy is used as the matrix material. Metal matrix composites were prepared by stir casting route. The composite was prepared by reinforcing 50 nm alumina nanoparticle so that the final composite contains 5, 10 and 15 wt.% alumina. Mechanical properties such as tensile strength, yield strength, impact strength and hardness were evaluated. Significant improvement was observed in impact strength and hardness value. The result showed that magnesium alloy with 5 wt.% alumina nanoparticle has a maximum impact strength of 25.2 J and hardness value 63.86 Hv respectively. Tensile strength and yield strength shows marginal increase in value.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Fabrication and Mechanical Properties of Alumina Nanoparticle Reinforced Magnesium Metal Matrix Composite by Stir Casting Method


    Weitere Titelangaben:

    Sae Technical Papers


    Beteiligte:

    Kongress:

    International Conference on Advances in Design, Materials, Manufacturing and Surface Engineering for Mobility ; 2018



    Erscheinungsdatum :

    2018-07-09




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    Experimental Investigation of Silicon Carbide Nanoparticles Reinforced Magnesium Alloy (AZ91E) Metal Matrix Composite by Vacuum Stir Casting Method

    Paramathma, Baskara Sethupathi / Jeyaseelan, Chandradass / Mahadevan, Kannan et al. | SAE Technical Papers | 2019


    Fabrication of aluminum metal matrix composite with carbon nanoparticles via stir casting

    Sawale, Alka / Reddy, Kancharla Harsha Vardhan / Poornashree, Kailash et al. | TIBKAT | 2021



    Design and Analysis of Hybrid Metal Matrix Composite Connecting Rod via Stir/Squeeze Casting Route

    Perumal, Ashokvarthanan / Soundarrajan, Karthik / Kuppuraj, Sathishkumar et al. | SAE Technical Papers | 2019


    Mode I Fatigue Crack Growth in a Continuous Alumina Fiber-Reinforced Magnesium Matrix Composite

    Nayeb-Hashemi, H. / Yang, Y. / Murphy, R. J. | British Library Online Contents | 1995