The gel fraction and the curing rate of the silver mirror protective film according to the curing condition were investigated. Two-packaged polyurethane dry film made from acryl polyol and three different isocyanate curing agents (HDI-biuret, HDI-trimer and IPDI trimer) were built on the silver mirror layer in order to protect the layer. FTIR/ATR spectra showed the isocyanate content was clearly decreased and the gel fraction was increased as curing temperature and time were increased. The optimum curing condition of the silver mirror protective film was 80□ and 30 minutes. The dry film prepared with the optimum condition satisfied all tests in our materials specification for automotive interior parts. Moreover, the pencil hardness of the film containing dibutyltin dilaurate was stronger than the film without catalyst.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Preparation and Physical Properties of Two-Packaged Polyurethane Coatings for Silver Mirror Layer Protection


    Weitere Titelangaben:

    Sae Technical Papers


    Beteiligte:
    Kim, Daeup (Autor:in) / Kim, Hyeondon (Autor:in) / Lee, Junghwan (Autor:in) / Kim, Ok (Autor:in) / Oh, Woojeong (Autor:in) / Kim, Yawon (Autor:in)

    Kongress:

    SAE World Congress & Exhibition ; 2009



    Erscheinungsdatum :

    2009-04-20




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    Chemical vapor deposited silica coatings for solar mirror protection

    GULINO, DANIEL / DEVER, THERESE / BANHOLZER, WILLIAM | AIAA | 1988


    Polyurethane rearview mirror heating device

    WU JINYAN / KONG ZHIYONG / SONG DINGGUO | Europäisches Patentamt | 2021

    Freier Zugriff


    VEHICLE MIRROR PROTECTION

    BANETTA LILLO GIANFRANCO | Europäisches Patentamt | 2018

    Freier Zugriff

    Pure silver mirror is durable

    British Library Online Contents | 2002