An investigation was made of factors contributing to maximum compressive residual stress. Stresses from furnace hardening heat treatment were shown to be highest at high hardness, medium carbon content, large section size, and minimum hardenability over the range investigated. Shot peening was found to decrease high heat treatment stresses. An example showed very high fatigue strength in plain carbon steel at high hardness which was related to the very high compressive residual stress induced by severe water quenching during heat treatment.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Residual Stresses in Quenched and Tempered Plain Carbon Steels


    Weitere Titelangaben:

    Sae Technical Papers


    Beteiligte:
    Nelson, D. V. (Autor:in) / Ricklefs, R. E. (Autor:in) / Evans, W. P. (Autor:in)

    Kongress:

    1971 Automotive Engineering Congress and Exposition ; 1971



    Erscheinungsdatum :

    1971-02-01




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch






    Fatigue Properties of Welded Roller-Quenched and Tempered (RQ) Steels

    Reemsnyder, Harold S. | SAE Technical Papers | 1979


    Fatigue properties of welded roller-quenched and tempered ( RQ ) steels

    Reemsnyder,H. / Bethlehem Steel,US | Kraftfahrwesen | 1979


    Residual Stresses in As-Quenched Aluminum Castings

    Xiao, Bowang / Li, Keyu / Wang, Qigui | SAE Technical Papers | 2008