This paper presents an approach in the context of intergranular corrosion process, its causes, effects and its direct relation with the Engineering, once the responsible professional shall consider the numerous losses that may be caused by this deterioration. The intergranular process of corrosion in stainless steel has been studied. A failure occurred by intergranular corrosion in service in Isolator Exhaust, which is critical to the functioning of the air diesel engine system. A microcrack was generated in the grain boundary region due the precipitation of complex carbides, which was aggravated by the working temperature. Given the working conditions of the isolator exhaust, it is suggested to replace the material AISI 304 with AISI 310, for it contains higher percentage of chromium, inhibiting intergranular corrosion occurrence.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    AISI 304 Steel Intergranular Corrosion (Failure Analysis)


    Weitere Titelangaben:

    Sae Technical Papers


    Beteiligte:

    Kongress:

    21st SAE Brasil International Congress and Exhibition ; 2012



    Erscheinungsdatum :

    2012-10-02




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch






    Predicting Mechanical Properties of Friction Welded AISI 1020/AISI 1018 Steel and AISI 431/AISI 1018 Steel Joints

    Visvalingam, Balasubramanian / Thirumalaikkannan, Dhamothara Kannan / Murugesan, Seeman et al. | SAE Technical Papers | 2023


    Corrosion of stainless steel AISI-440C in hydrated ethanol fuel

    Aguiar,A. / Alarcon,O.Q. / Teschke,O. et al. | Kraftfahrwesen | 1988


    Microscopy study of intergranular stress corrosion cracking of X-52 line pipe steel

    Elboujdaini, M. / Li, J. / Fang, B. et al. | Tema Archiv | 2006