The tensile and fatigue strengths of squeeze cast metal matrix composites (MMC's) containing 0 and 15 volume percent of discontinuous Fiberfrax® ceramic fibers in an F332 T5 aluminum alloy matrix were determined at room temperature and 350°C. Rotating beam fatigue testing was performed using the up-and-down modified staircase method to determine the fatigue strength of these composites for 50% probability of failure at 107 cycles.Significant improvements in tensile and fatigue strengths were measured for the MMC material compared to the unreinforced alloy. The statistical variation in the measured fatigue strengths of the MMC material was equivalent to that of the unreinforced alloy, indicating the high degree of reproducibility of the manufacturing process.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Fatigue Behavior of Squeeze Cast Metal Matrix Composites for Diesel Pistons


    Weitere Titelangaben:

    Sae Technical Papers


    Beteiligte:
    Budinger, B.O. (Autor:in) / Chi, F.K. (Autor:in) / Smalc, M.D. (Autor:in) / Maier, R.D. (Autor:in) / Krucek, T.W. (Autor:in)

    Kongress:

    International Congress & Exposition ; 1992



    Erscheinungsdatum :

    01.02.1992




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    Fatigue behavior of squeeze cast metal matrix composites for diesel pistons

    Maier,R.D. / Smalc,M.D. / Krucek,T.W. et al. | Kraftfahrwesen | 1992


    Squeeze Cast Diesel Pistons

    McGuire,M.F. / Gould,US | Kraftfahrwesen | 1979



    Elevated Temperature Mechanical Properties of Squeeze Cast Metal Matrix Composites for Diesel Pistons

    Budinger, B. O. / Chi, F. K. / Smalc, M. D. et al. | SAE Technical Papers | 1993


    Squeeze Cast Pistons

    Online Contents | 1994