The effects of single and multiple tensile overloads on precracked center-notched sheet specimens of Ti-8 Al-1 Mo-1V titanium alloy were investigated under laboratory conditions. Single tensile overloads always delayed subsequent fatigue crack growth at lower stress levels. Multiple tensile overloads caused a delay in fatigue crack growth greater than a single overload, with the amount depending on the number of overloads. The quantitative values of fatigue crack growth delay are reported for overloads ranging from 116-233%. Single intermittent overloads applied within the delay caused by previous overloads produced the greatest delays. Conditions subsequent to overloading and encountered in realistic environment-including time at zero load, temperature, and a seawater environment-were found to reduce the delay effects greatly and should be incorporated into theoretical models. These effects are explained in terms of fatigue crack closure concepts.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Fatigue Crack Growth Delays


    Weitere Titelangaben:

    Sae Technical Papers


    Beteiligte:

    Kongress:

    1974 Automotive Engineering Congress and Exposition ; 1974



    Erscheinungsdatum :

    01.02.1974




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    Fatigue Crack Growth Delays

    Dubensky, R. | Tema Archiv | 1974


    Fatigue-Crack-Growth Computer Program

    Forman, Royce G. / Shivakumar, V. / Newman, James C., Jr. | NTRS | 1991


    Fatigue-Crack-Growth Structural Analysis

    Newman, J. C., Jr. | NTRS | 1986


    Fatigue Crack Growth in Pavements

    Castell, M. A. / Ingraffea, A. R. / Irwin, L. H. | British Library Online Contents | 2000